Trench epitaxial growth for a FinFET device having reduced capacitance

ABSTRACT

A FinFET device includes a semiconductor fin, a gate electrode extending over a channel of the fin and sidewall spacers on each side of the gate electrode. A dielectric material is positioned on each side of a bottom portion of said fin, with an oxide material on each side of the fin overlying the dielectric material. A recessed region, formed in the fin on each side of the channel region, is delimited by the oxide material. A raised source region fills the recessed region and extends from the fin on a first side of the gate electrode to cover the oxide material to a height which is in contact with the sidewall spacer. A raised drain region fills the recessed region and extends from the fin on a second side of the gate electrode to cover the oxide material to a height which is in contact with the sidewall spacer.

TECHNICAL FIELD

The present invention relates to the fabrication of integrated circuitsand, more particularly, to a process for the formation of FinFET-typeintegrated circuit devices and a FinFET device produced by such aprocess.

BACKGROUND

A FinFET transistor utilizes a channel region which is oriented toconduct an electrical current parallel to the surface of the substrate.The channel region is provided in an elongated section of semiconductormaterial referred to in the art as a “fin.” The source and drain regionsof the transistor are typically also formed in the elongated section oneither side of the channel region. A gate is placed over and on bothopposed sides of the elongated section at the location of the channelregion to provide control over the conductive state of the transistor.This FinFET design is well suited for manufacturing a multi-channeltransistor in which multiple elongated sections are formed in parallelto define neighboring channel regions separated from each other by anintermediate gate portion, where the transistor gate spans with aperpendicular orientation over the multiple elongated sections.

It is well known in the art to form the source and drain regions of thetransistor using epitaxial growth starting from a top surface of the finon either side of the gate and channel region. There are number ofbenefits which accrue from the use of a tall epitaxial growth. First,because of the generally tapered shape of the sidewall spacers for thegate structure, the width between adjacent gate structures increaseswith height, and thus a taller epitaxial growth will result in a largersurface area at the top of the epitaxial growth for use in silicidingthe source or drain contact. Second, increased epitaxial growth heightmakes the circuit more robust to issues with contact gouging. Third, theprofile of the contact etch bottom profile into the epitaxial growth canbe tuned to increase contact area if a greater epitaxial growth heightis available. Fourth, increased epitaxial growth provides more materialfor consumption during a salicidation process associated with formingthe source/drain contacts. Fifth, there is a lessened risk of shorting.Sixth, the top surface of the epitaxial growth could be patterned withchannels or other depth structures to increase the contact area and areaavailable for salicidation.

However, the growth of taller epitaxial regions for the source and drainon the top surface of the fin can violate design spacing rules. There isaccordingly a need in the art for a method to better confine epitaxialgrowth for source and drain regions of FinFET transistor in a mannerwhich permits a taller epitaxial growth with reduced risk of violatingdesign spacing rules.

SUMMARY

In an embodiment, an integrated FinFET transistor circuit comprises: afin of semiconductor material; a transistor gate electrode extendingover a channel region of said fin; sidewall spacers on each side of thetransistor gate electrode; wherein said fin further includes a recessedregion on each side of the channel region; an oxide material on eachside of each recessed region in the fin; a raised source region ofepitaxial growth material filling said recessed region and extendingfrom said fin on a first side of the transistor gate electrode to coverthe oxide material to a height above said fin and in contact with thesidewall spacer; and a raised drain region of said epitaxial growthmaterial filling said recessed region and extending from said fin on asecond side of the transistor gate electrode to cover the oxide materialto said height above said fin and in contact with the sidewall spacer.

In an embodiment, a method for manufacturing a FinFET transistor,comprises: forming a fin of semiconductor material; forming a transistorgate structure that extends over a channel region of said fin; formingsidewall spacers on each side of the transistor gate electrode;depositing an oxide material on each side of the fin; forming recessedregions at a top of the fin adjacent the channel region on each side ofthe transistor gate electrode, wherein said oxide material is present oneach side of the recessed regions; and epitaxially growing epitaxialgrowth material from said fin to fill the recessed regions and extendfrom said fin to form a raised source region on one side of thetransistor gate structure to cover the oxide material to a height abovesaid fin and in contact with the sidewall spacer and form a raised drainregion on another side of the transistor gate structure to cover theoxide material to said height above said fin and in contact with thesidewall spacer.

In an embodiment, an integrated FinFET transistor circuit, comprises: afin of semiconductor material; a dielectric material on each side of abottom portion of said fin; an oxide material on each side of said finabove the dielectric material; a transistor gate electrode extendingover a channel region of said fin; sidewall spacers on each side of thetransistor gate electrode; wherein said fin further includes a recessedregion on each side of the channel region, with said oxide material oneach side of each recessed region in the fin; a raised source region ofepitaxial growth material filling said recessed region and extendingfrom said fin on a first side of the transistor gate electrode to coverthe oxide material to a height above said fin and in contact with thesidewall spacer; and a raised drain region of said epitaxial growthmaterial filling said recessed region and extending from said fin on asecond side of the transistor gate electrode to cover the oxide materialto said height above said fin and in contact with the sidewall spacer.

BRIEF DESCRIPTION OF THE DRAWINGS

For a better understanding of the embodiments, reference will now bemade by way of example only to the accompanying figures in which:

FIGS. 1-12 show process steps for the formation of an integrated circuitincluding FinFET devices;

FIGS. 13-15 show process steps relating to a modification of the processof FIGS. 1-12; and

FIGS. 16A-23 show process steps for the formation of another integratedcircuit including FinFET devices.

DETAILED DESCRIPTION OF THE DRAWINGS

Reference is now made to FIGS. 1-12 showing process steps for theformation of an integrated circuit including FinFET devices. It will beunderstood that the illustrations provided do not necessarily show thefeatures drawn to scale.

The process starts with a substrate 10 as shown in FIG. 1. The substrate10 may comprise a silicon on insulator (SOI) substrate wafer of aconventional type (including an extremely thin silicon on insulator(ETSOI) or ultra-thin body and buried oxide (UTBB) silicon on insulator(SOI) known to those skilled in the art). Alternatively, the substrate10 may comprise a bulk semiconductor substrate wafer. The topsemiconductor layer of the SOI substrate or the semiconductor materialof the bulk substrate may be doped as appropriate for the integratedcircuit application (and in the present implementation the substratematerial which will eventually be formed into a fin need not be doped atall). In an embodiment of an SOI substrate, the top semiconductor layermay be of the fully depleted (FD) configuration. The bulk substrate mayinclude, for example, a number of epitaxially grown semiconductorlayers. The process techniques described herein are equally applicableto SOI and bulk substrates, as well as other types of substrate, andthus a generic representation of the substrate 10 is shown in FIG. 1 andreferenced throughout the description.

Using fabrication techniques well known to those skilled in the art, aplurality of fins 12 of semiconductor material are formed at the topsurface of the substrate 10. The result of the fin fabrication processis shown in cross-sectional FIGS. 2A and 2B, wherein the illustratedorientations of FIGS. 2A and 2B are orthogonal to each other. The fins12 may, for example, be made of silicon, silicon-germanium, or othersuitable semiconductor materials. The fins 12 may, for example, be dopedas appropriate for the integrated circuit application. The fins may beseparated from each other by a dielectric or other insulating material22.

An example of the process for fin fabrication is shown in FIGS. 3A-3G.In FIG. 3A, a hard mask layer 14 (for example, of silicon nitride SiN)is deposited on the substrate 10. Over the hard mask layer 14, alithographically patterned mask 16 is formed on the hard mask layer 14.The mask 16 includes a number of mask openings 18 with the lithographicpatterning leaving mask material at locations where fins 12 are desired.An etching operation is then performed through the openings 18 to definea plurality of apertures 20 in the top surface of the substrate 10 whichdefine the fins 12. The lithographically patterned mask 16 is thenremoved as shown in FIG. 3C. A dielectric material 22 is then depositedto fill the apertures 20 as shown in FIG. 3D. An upper portion of thedielectric material 22 is then removed through a recessing operation toexpose the remaining portions of the hard mask layer 14 as shown in FIG.3E. The remaining portions of the hard mask layer 14 are then strippedaway as shown in FIG. 3F. The upper portion of the remaining dielectricmaterial 22 is then partially recessed to expose the upper portions ofthe fins 12 as shown in FIG. 3G.

The individual fins 12 may have an exposed height “h” of 20-50 nm and awidth “w” of 6-12 nm. The length “l” of each fin 12 is determined by theapplication of the transistor and may, for example, be 0.06 to 600 μm.

Reference is now made to FIGS. 4A-4C. A sacrificial polysilicon material40 is deposited using a conventional chemical vapor deposition (CVD)process on the substrate 10 to cover the fins 12 (and the dielectric22). The polysilicon material 40 may, in an alternative implementation,instead comprise amorphous silicon. A conformal oxide (not explicitlyshown) may be formed on the exposed surfaces of the fins 12 prior todeposition of the polysilicon material 40. As understood by thoseskilled in the art, the polysilicon material (with the oxide) areassociated with the formation of structures commonly referred to as“dummy gate” structures. The polysilicon material of the dummy gatestructures will be subsequently removed later in the fabrication processand replaced with a metal gate stack defining the actual operating gateelectrode for the transistor devices (this process referred to in theart as a “replacement metal gate (RMG)” process). Thus, there is no needto dope the polysilicon material 40. The deposit of the polysiliconmaterial 40 will have a height in excess of the height of the fins 12 sothat the fins will be completely covered. The material 40 may have athickness, for example, of 50-150 nm. The top surface of the polysiliconmaterial 40 deposit is polished using conventional chemical-mechanicalplanarization (CMP) techniques to provide a planar top surface.

A hard mask layer 42 with a thickness of 30-60 nm is deposited on theplanar top surface of the polysilicon material 40 using a chemical vapordeposition (CVD) process. The layer 42 is lithographically patterned ina manner well known to those skilled in the art to leave mask material44 at desired locations for the dummy gate structures. A reactive ionetch (RIE) is then performed to open apertures 46 in the polysiliconmaterial on either side of the dummy gate 48. The structure of the dummygate 48 may be considered to straddle over a fin 12, or over a pluralityof adjacent fins, at a channel region (see, FIG. 4A).

A silicon nitride material is then conformally deposited, for example,using an atomic layer deposition (ALD) technique as known in the art,and subsequently etched preferentially on the horizontal surfaces toleave sidewall spacers 50 on the side walls of the polysilicon dummygates 48 (see, FIG. 4B). In one implementation, the etch will remove allsilicon nitride material from the fins 12 as shown in FIG. 4C. For analternatively implementation, see FIG. 13 and the discussion below.

The dummy gate structure accordingly comprises a patterned polysilicon(or amorphous silicon) dummy gate 48, an overlying silicon nitride cap(formed by the mask material 44) and sidewall spacers 50.

It will be noted in FIG. 4B that gate structures have also been formedat the ends of the fin 12 in accordance with the known technique of gatetuck-under. Without this structure, the subsequent formation of raisedsource/drain structures (described below) could result in epitaxialgrowth in an outward direction resulting in an increased risk ofshorting to an adjacent structure. Additionally, these end structuresensure better quality and consistency of epitaxial growth which mayexhibit an non-uniform growth at the ends of the fin in the absence ofthe end structures.

Reference is now made to FIGS. 5A-5C. A silicon dioxide material 80 isdeposited to cover the substrate. The material 80 may be furtherprocessed using conventional chemical-mechanical planarization (CMP)techniques to provide a planar top surface that stops at the top of eachdummy gate structure.

A hard mask layer 110, for example an organic planarization layer (OPL)having a thickness of 100-2000 nm, is then deposited on the planar topsurface of the silicon dioxide material 80 layer using a coatingprocess. The layer 110 is lithographically patterned in a manner wellknown to those skilled in the art to form openings 112 at desiredlocations for source and drain regions, respectively, of the transistor.The result is shown in FIGS. 6A-6C.

A reactive ion etch (RIE) is then performed through the mask openings112 to open apertures 114 in the silicon dioxide material 80 layer whichextend down to expose a top surface 116 of the fins 12. The result isshown in FIGS. 7A-7B. A cross-section corresponding to FIG. 6A is notpresented since the layer 110 prevents etching at that location.

Reference is now made to FIGS. 8A-8B. An etch is then performed torecess 60 the fins 12 on either side of the dummy gate structures. Theetch may, for example, comprise an anisotropic (HBr) etch. The depth “d”of the recess 60 may, for example, comprise 20-40 nm. In an embodiment,the recess may extend to a depth equal to a height of the dielectricmaterial 22. The portion 62 of the fin 12 located under the dummy gates48 between the recess 60 regions defines a channel region of the FinFETtransistor. In an embodiment, the channel region 62 may have a length 64of 15-30 nm.

The amount of the depth d may matter in some applications. The deeperthe depth d, the closer the resulting in situ doped source/drain can getto the channel region 62 so as to form a more abrupt junction. However,if a strained channel material is used, the deeper the depth d the moreof the material that is cut which can lead to a reduction in the appliedstrain on the channel. So, selection of the depth d is an importantconsideration for the transistor designer so as to balance betweenjunction design and strain retention. Thus, it will be understood thatthe illustration of the depth d in FIGS. 8A-8B is an example of a depthchosen in accordance with this balancing evaluation.

A stripping process is then performed to remove the hard mask layer 110.The result is shown in FIGS. 9A-9B.

Using an epitaxial process tool and starting from the exposed topsurface of the fins 12 in the recess 60 region, an epitaxial growth 70of a silicon-based semiconductor material is made. The epitaxial growth70 not only fills the recess 60 regions (adjacent the channel portion62) but further extends above the previous top surface of the fins toregions adjacent the sidewall spacers 50 on either side of the dummygate structures and is confined within the apertures 114 with a heightthat is preferably less than the height of the sacrificial polysilicondummy gate 48. The silicon-based epitaxial growth 70 may be in situdoped as needed for a given application. As a result of the epitaxialgrowth 70, raised source and drain regions 72 and 74, respectively, areformed on either side of the dummy gate structures. The result is shownin FIGS. 10A-10B. The epitaxial growth 70 may comprise, for example:silicon doped with boron or indium; silicon-germanium doped with boronor indium; silicon doped with phosphorous or arsenic; or silicon-carbidedoped with phosphorous or arsenic. It will be understood that differentregions of the substrate may utilize different materials for theepitaxial growth to account for, for example, the need to maketransistors of the n-channel or p-channel type.

Reference is now made to FIGS. 11A-11B. A silicon dioxide material 82 isdeposited to cover the substrate and fill any remaining portions of theapertures 114. The material 82 may be further processed usingconventional chemical-mechanical planarization (CMP) techniques toprovide a planar top surface that stops at the top of each dummy gate48.

Using a selective removal process (such as an ammonium hydroxide etch),the dummy gates 48 are removed. The removed dummy gates 48 are thenreplaced with a metal gate structure 90. In an example, the metal gatestructure may comprise a high-K dielectric liner (forming the gatedielectric for the transistor) deposited using an atomic layerdeposition (ALD) process with a thickness of 1-2 nm, a work functionmetal deposited using a chemical vapor deposition process and a contactmetal fill deposited using a chemical vapor deposition process. Aninsulating cap 92 covers the metal gate structure 90. The result isshown in FIG. 12.

Further processing well known to those skilled in the art is thenperformed to produce the metal contacts to the gate (metal gatestructure 90), source region 72 and drain region 74.

At this point, front end of line (FEOL) fabrication of the integratedcircuit is complete. Further back end of line (BEOL) processing tofabricate metallizations and interconnects may then be performed as wellknown to those skilled in the art.

Reference is now once again made to FIGS. 4A-4C. As discussed above, asilicon nitride material is conformally deposited, for example, using anatomic layer deposition (ALD) technique as known in the art, on thesubstrate and subsequently etched to leave sidewall spacers 50 only onthe side walls of the polysilicon dummy gates 48. If the etch does not,however, completely remove the silicon nitride material from thesidewalls of the fins 12, fin sidewall spacers 50′ will be left on thesidewalls of the fins. This is shown in FIG. 13 (which corresponds toFIG. 4C prior to the etch) and FIG. 14 (which corresponds to FIG. 5Cafter the etch). As a result, the fins 12 and epitaxial growth 70 in therecesses 60 will be delimited by the fin sidewall spacers 50′ as shownin FIG. 15 (which corresponds to FIG. 11B).

Reference is now made to FIGS. 1-3G and 16A-23 showing process steps forthe formation of another integrated circuit including FinFET devices. Itwill be understood that the illustrations provided do not necessarilyshow the features drawn to scale.

The description of FIGS. 1-3G is provided above and is incorporatedherein by reference.

Reference is now made to FIGS. 16A-16C. A sacrificial polysiliconmaterial 40 is deposited using a conventional chemical vapor deposition(CVD) process on the substrate 10 to cover the fins 12 (and thedielectric 22). The polysilicon material 40 may, in an alternativeimplementation, instead comprise amorphous silicon. A conformal oxide(not explicitly shown) may be formed on the exposed surfaces of the fins12 prior to deposition of the polysilicon material 40. As understood bythose skilled in the art, the polysilicon material (with the oxide) areassociated with the formation of structures commonly referred to as“dummy gate” structures. The polysilicon material of the dummy gatestructures will be subsequently removed later in the fabrication processand replaced with a metal gate stack defining the actual operating gateelectrode for the transistor devices (this process referred to in theart as a “replacement metal gate (RMG)” process). Thus, there is no needto dope the polysilicon material 40. The deposit of the polysiliconmaterial 40 will have a height in excess of the height of the fins 12 sothat the fins will be completely covered. The material 40 may have athickness, for example, of 50-150 nm. The top surface of the polysiliconmaterial 40 deposit is polished using conventional chemical-mechanicalplanarization (CMP) techniques to provide a planar top surface.

A hard mask layer 42 with a thickness of 30-60 nm is deposited on theplanar top surface of the polysilicon material 40 using a chemical vapordeposition (CVD) process. The layer 42 is lithographically patterned ina manner well known to those skilled in the art to leave mask material44 at desired locations for the dummy gate structures. A reactive ionetch (RIE) is then performed to open apertures 46 in the polysiliconmaterial on either side of the dummy gate 48. The structure of the dummygate 48 may be considered to straddle over a fin 12, or over a pluralityof adjacent fins, at a channel region (see, FIG. 16A).

A silicon nitride material 150 is deposited, for example, using anatomic layer deposition (ALD) technique as known in the art, on thesubstrate. This material 150 covers the fins 12, the patternedpolysilicon (or amorphous silicon) dummy gate 48, the overlying siliconnitride cap (formed by the mask material 44) and the dielectric material22. In the embodiment shown in FIGS. 4A-4C, a subsequent etch isperformed which removes a substantial portion of the material 150 so toleave, for example, sidewall spacers 50 on the sidewalls of the dummygate structure. In the embodiment associated with FIGS. 16A-16C,however, the etch is not performed so as to leave the conformal material150 deposit in place.

Reference is now made to FIGS. 17A-17C. A silicon dioxide material 80 isdeposited to cover the substrate. The material 80 may be furtherprocessed using conventional chemical-mechanical planarization (CMP)techniques to provide a planar top surface that stops at the top of eachdummy gate structure.

A hard mask layer 110, for example an organic planarization layer (OPL)having a thickness of 100-2000 nm, is then deposited on the planar topsurface of the silicon dioxide material 80 layer using a coatingprocess. The layer 110 is lithographically patterned in a manner wellknown to those skilled in the art to form openings 112 at desiredlocations for source and drain regions, respectively, of the transistor.The result is shown in FIGS. 18A-18C.

A reactive ion etch (RIE) is then performed through the mask openings112 to open apertures 114 in the silicon dioxide material 80 layer whichextend down to expose a top surface 116 of the fins 12. The result isshown in FIGS. 19A-19B. A cross-section corresponding to FIG. 18A is notpresented since the layer 110 prevents etching at that location.

Reference is now made to FIGS. 20A-20B. A further etch is then performedto recess the layer 150, which causes the production of the sidewallspacers 50 (in the apertures 114), and to recess 60 the fins 12 oneither side of the dummy gate structures, wherein the recessing of thelayer 150 removes material from either side of the fin 12 as well suchthat the recess 60 is wider than the fin as shown at reference 62. Theetch may, for example, comprise an anisotropic (HBr) etch. The depth “d”of the recess 60 may, for example, comprise 20-40 nm. In an embodiment,the recess may extend to a depth equal to a height of the dielectricmaterial 22. The portion 62 of the fin 12 located under the dummy gates48 between the recess 60 regions defines a channel region of the FinFETtransistor. In an embodiment, the channel region 62 may have a length 64of 15-30 nm.

A stripping process is then performed to remove the hard mask layer 110.The result is not shown, but may be understood by cross-reference toFIGS. 9A-9B.

Using an epitaxial process tool and starting from the exposed topsurface of the fins 12 in the recess 60 region, an epitaxial growth 70of a silicon-based semiconductor material is made. The epitaxial growth70 not only fills the recess 60 regions (adjacent the channel portion62) but further extends above the previous top surface of the fins toregions adjacent the sidewall spacers 50 on either side of the dummygate structures and is confined within the apertures 114 with a heightthat is preferably less than the height of the sacrificial polysilicondummy gate 48. The silicon-based epitaxial growth 70 may be in situdoped as needed for a given application. As a result of the epitaxialgrowth 70, raised source and drain regions 72 and 74, respectively, areformed on either side of the dummy gate structures. The result is shownin FIGS. 21A-21B. The epitaxial growth 70 may comprise, for example:silicon doped with boron or indium; silicon-germanium doped with boronor indium; silicon doped with phosphorous or arsenic; or silicon-carbidedoped with phosphorous or arsenic. It will be understood that differentregions of the substrate may utilize different materials for theepitaxial growth to account for, for example, the need to maketransistors of the n-channel or p-channel type.

Reference is now made to FIGS. 22A-22B. A silicon dioxide material 82 isdeposited to cover the substrate and fill remaining portions of theapertures 114. The material 82 may be further processed usingconventional chemical-mechanical planarization (CMP) techniques toprovide a planar top surface that stops at the top of each dummy gate48.

Using a selective removal process (such as an ammonium hydroxide etch),the dummy gates 48 are removed. The removed dummy gates 48 are thenreplaced with a metal gate structure 90. In an example, the metal gatestructure may comprise a high-K dielectric liner (forming the gatedielectric for the transistor) deposited using an atomic layerdeposition (ALD) process with a thickness of 1-2 nm, a work functionmetal deposited using a chemical vapor deposition process and a contactmetal fill deposited using a chemical vapor deposition process. Aninsulating cap 92 covers the metal gate structure 90. The result isshown in FIG. 23.

Further processing well known to those skilled in the art is thenperformed to produce the metal contacts to the gate (metal gatestructure 90), source region 72 and drain region 74.

At this point, front end of line (FEOL) fabrication of the integratedcircuit is complete. Further back end of line (BEOL) processing tofabricate metallizations and interconnects may then be performed as wellknown to those skilled in the art.

Although making and using various embodiments are discussed in detailherein, it should be appreciated that as described herein are providedmany inventive concepts that may be embodied in a wide variety ofcontexts. Embodiments discussed herein are merely representative and donot limit the scope of the invention.

While the invention has been illustrated and described in detail in thedrawings and foregoing description, such illustration and descriptionare considered illustrative or exemplary and not restrictive; theinvention is not limited to the disclosed embodiments. Other variationsto the disclosed embodiments can be understood and effected by thoseskilled in the art in practicing the claimed invention, from a study ofthe drawings, the disclosure, and the appended claims.

What is claimed is:
 1. An integrated FinFET transistor circuit,comprising: a fin of semiconductor material; a transistor gate electrodeextending over a channel region of said fin; sidewall spacers on eachside of the transistor gate electrode; wherein said fin further includesa recessed region on each side of the channel region; an oxide materialon each side of each recessed region in the fin; a raised source regionof epitaxial growth material filling said recessed region and extendingfrom said fin on a first side of the transistor gate electrode to coverthe oxide material to a height above said fin and in contact with thesidewall spacer; and a raised drain region of said epitaxial growthmaterial filling said recessed region and extending from said fin on asecond side of the transistor gate electrode to cover the oxide materialto said height above said fin and in contact with the sidewall spacer;wherein said height is greater than a height of the transistor gateelectrode.
 2. The circuit of claim 1, further comprising a dielectricmaterial on each side of a bottom portion of said fin, wherein saidoxide material on each side of each recessed region in the fin ispositioned above said dielectric material.
 3. The circuit of claim 1,further including fin sidewall spacers on each side the fin and therecessed region, wherein said fin sidewall spacers are positionedbetween the oxide material on each side of each recessed region in thefin and the recessed region.
 4. The circuit of claim 1, wherein thesidewall spacers extend underneath the oxide material.
 5. The circuit ofclaim 1, further comprising a dielectric material on each side of abottom portion of said fin, wherein said sidewall spacers extend on eachside of the fin above the bottom portion, and wherein the oxide materialon each side of each recessed region in the fin is positioned above saidsidewall spacers.
 6. The circuit of claim 1, wherein a width of theraised source and drain regions increases with increased height of theraised source and drain regions.
 7. The circuit of claim 1, furthercomprising a dielectric material on each side of a bottom portion ofsaid fin, wherein said recessed regions in the fin have a depth whichextends to a height of the dielectric material.
 8. An integrated FinFETtransistor circuit, comprising: a fin of semiconductor material; adielectric material on each side of a bottom portion of said fin; anoxide material on each side of said fin above the dielectric material; atransistor gate electrode extending over a channel region of said fin;sidewall spacers on each side of the transistor gate electrode; whereinsaid fin further includes a recessed region on each side of the channelregion, with said oxide material on each side of each recessed region inthe fin; a raised source region of epitaxial growth material fillingsaid recessed region and extending from said fin on a first side of thetransistor gate electrode to cover the oxide material to a height abovesaid fin and in contact with the sidewall spacer; and a raised drainregion of said epitaxial growth material filling said recessed regionand extending from said fin on a second side of the transistor gateelectrode to cover the oxide material to said height above said fin andin contact with the sidewall spacer; wherein the sidewall spacers extendon each side of the fin above the bottom portion, and wherein the oxidematerial on each side of each recessed region in the fin is positionedabove said sidewall spacers.
 9. The circuit of claim 8, furthercomprising fin sidewall spacers on each side the fin and the recessedregion, wherein said fin sidewall spacers are positioned between theoxide material on each side of each recessed region in the fin and therecessed region.
 10. The circuit of claim 8, wherein said recessedregions in the fin have a depth which extends to a height of thedielectric material.
 11. The circuit of claim 8, wherein a width of theraised source and drain regions increases with increased height of theraised source and drain regions, and said height is greater than aheight of the transistor gate electrode.
 12. An integrated FinFETtransistor circuit, comprising: a fin of semiconductor material; atransistor gate electrode extending over a channel region of said fin; asidewall spacer on a side of the transistor gate electrode; wherein saidfin further includes a recessed region; an oxide material on each sideof the recessed region; a raised region of epitaxial growth materialfilling said recessed region and extending from said fin to cover theoxide material to a height above said fin and in contact with thesidewall spacer; wherein said height is greater than a height of thetransistor gate electrode.
 13. The circuit of claim 12, wherein theraised region is one of a source region or a drain region.
 14. Thecircuit of claim 12, further comprising a dielectric material on eachside of a bottom portion of said fin, wherein said oxide material on therecessed region is positioned above said dielectric material.
 15. Thecircuit of claim 12, further including a further sidewall spacer on thefin, wherein said further sidewall spacer is positioned between theoxide material and the recessed region.
 16. The circuit of claim 12,wherein a width of the raised region increases with increased height ofthe raised region.
 17. An integrated FinFET transistor circuit,comprising: a fin of semiconductor material; a transistor gate electrodeextending over a channel region of said fin; sidewall spacers on eachside of the transistor gate electrode; wherein said fin further includesa recessed region on each side of the channel region; an oxide materialon each side of each recessed region in the fin, wherein the sidewallspacers extend underneath the oxide material; a raised source region ofepitaxial growth material filling said recessed region and extendingfrom said fin on a first side of the transistor gate electrode to coverthe oxide material to a height above said fin and in contact with thesidewall spacer; and a raised drain region of said epitaxial growthmaterial filling said recessed region and extending from said fin on asecond side of the transistor gate electrode to cover the oxide materialto said height above said fin and in contact with the sidewall spacer.18. The circuit of claim 17, further comprising a dielectric material oneach side of a bottom portion of said fin, wherein said oxide materialon each side of each recessed region in the fin is positioned above saiddielectric material.
 19. The circuit of claim 17, further including finsidewall spacers on each side the fin and the recessed region, whereinsaid fin sidewall spacers are positioned between the oxide material oneach side of each recessed region in the fin and the recessed region.20. The circuit of claim 17, further comprising a dielectric material oneach side of a bottom portion of said fin, wherein said sidewall spacersextend on each side of the fin above the bottom portion, and wherein theoxide material on each side of each recessed region in the fin ispositioned above said sidewall spacers.
 21. The circuit of claim 17,wherein a width of the raised source and drain regions increases withincreased height of the raised source and drain regions.
 22. The circuitof claim 17, further comprising a dielectric material on each side of abottom portion of said fin, wherein said recessed regions in the finhave a depth which extends to a height of the dielectric material. 23.An integrated FinFET transistor circuit, comprising: a fin ofsemiconductor material; a transistor gate electrode extending over achannel region of said fin; sidewall spacers on each side of thetransistor gate electrode; wherein said fin further includes a recessedregion on each side of the channel region; an oxide material on eachside of each recessed region in the fin; a raised source region ofepitaxial growth material filling said recessed region and extendingfrom said fin on a first side of the transistor gate electrode to coverthe oxide material to a height above said fin and in contact with thesidewall spacer; a raised drain region of said epitaxial growth materialfilling said recessed region and extending from said fin on a secondside of the transistor gate electrode to cover the oxide material tosaid height above said fin and in contact with the sidewall spacer; anda dielectric material on each side of a bottom portion of said fin,wherein said sidewall spacers extend on each side of the fin above thebottom portion, and wherein the oxide material on each side of eachrecessed region in the fin is positioned above said sidewall spacers.24. The circuit of claim 23, further comprising a dielectric material oneach side of a bottom portion of said fin, wherein said oxide materialon each side of each recessed region in the fin is positioned above saiddielectric material.
 25. The circuit of claim 23, further including finsidewall spacers on each side the fin and the recessed region, whereinsaid fin sidewall spacers are positioned between the oxide material oneach side of each recessed region in the fin and the recessed region.26. The circuit of claim 23, wherein a width of the raised source anddrain regions increases with increased height of the raised source anddrain regions.
 27. The circuit of claim 23, further comprising adielectric material on each side of a bottom portion of said fin,wherein said recessed regions in the fin have a depth which extends to aheight of the dielectric material.
 28. An integrated FinFET transistorcircuit, comprising: a fin of semiconductor material; a dielectricmaterial on each side of a bottom portion of said fin; an oxide materialon each side of said fin above the dielectric material; a transistorgate electrode extending over a channel region of said fin; sidewallspacers on each side of the transistor gate electrode; wherein said finfurther includes a recessed region on each side of the channel region,with said oxide material on each side of each recessed region in thefin; a raised source region of epitaxial growth material filling saidrecessed region and extending from said fin on a first side of thetransistor gate electrode to cover the oxide material to a height abovesaid fin and in contact with the sidewall spacer; and a raised drainregion of said epitaxial growth material filling said recessed regionand extending from said fin on a second side of the transistor gateelectrode to cover the oxide material to said height above said fin andin contact with the sidewall spacer; wherein a width of the raisedsource and drain regions increases with increased height of the raisedsource and drain regions, and said height is greater than a height ofthe transistor gate electrode.
 29. The circuit of claim 28, furthercomprising fin sidewall spacers on each side the fin and the recessedregion, wherein said fin sidewall spacers are positioned between theoxide material on each side of each recessed region in the fin and therecessed region.
 30. The circuit of claim 28, wherein said recessedregions in the fin have a depth which extends to a height of thedielectric material.